Type I
Type I
Tandis Parseh is one of the prominent trading companies promoting white clinker Type I-425 and Clinker Type II to local and international markets as it is the main ingredient in cement production.
Clinker type I is used for the production of ordinary Portland type I cement, which is the most common type of cement produced and commonly used worldwide. It is used for all common drives, such as making concrete, mortar, and plaster. Clinker type II I is used to producing moderate heat Cement.
Clinker minerals react with water to produce the hydrates that are responsible for cement’s setting and strength-giving properties. Tandis Parseh can supply high-quality Clinker Type I & II in bulk packaging per client requirement.
APPLICATIONS:
Used to produce grey and white cement
Used as binder in cement productsClinker Specification Type 1 COMPOSITION % TEST METHOD VALUE STANDARD LIMIT SiO2 ASTM C-114 20 – 22 – Al2O3 ASTM C-114 5.60 – 5.95 – Fe2O3 ASTM C-114 3.3 – 4 – CaO ASTM C-114 64.40 – 66 – MgO ASTM C-114 3 – 3.7 Max 5.0 SO3 ASTM C-114 0.25 – 0.75 – K2O ASTM C-114 0.80 – Na2O ASTM C-114 0.35 – CL ASTM C-114 – – LOI ASTM C-114 0.20 – 0.50 Max 1.0 IR ASTM C-114 020 – 040 Insol. Res. – LSF ASTM C-114 93 – 96 – SiM ASTM C-114 2.44 – AIM ASTM C-114 1.65 – 1.80 – C3S ASTM C-114 55 – 62 – C2S ASTM C-114 15 – 20 – C3A ASTM C-114 8 – 10 – C4AF ASTM C-114 9 – 10.50 – Free CaO ASTM C-114 0.70 – 1.70 Max 2.0 Total Alkali as Na2O ASTM C-114 0.80 – 1.1 – Clinker Sieve Analysis Size (mm) ASTM E11 Unit (percent) 0 – 5 mm % 5 5 -10 mm % 20 10 -20 mm % 30 20 -30 mm % 20 30 – 50 mm % 25 Clinker specification Type II COMPONENT KMCC Range ASTM C 150 BS EN 197-1
SIO2 22.00 AL2O3 5.00 Fe2O3 3.80 CaO 65.50 MgO 2.20 SO3 0.10-1.00 K2O 0.60 Na2O 0.30 Cl 0.00-0.025 L.O. I 0.50 I.R 0.30 LSF 93.50 SIM 2.40 ALM 1.20 C3S 60.00 C2S 17.00 C3A 6.00 C4AF 12.00 Free CaO 1.00
Product Picture